Norfor® 130 GF/20 NATURALE 0507
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | SO.F.TER. SPA |
| Trademark: | Norfor® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRceTL_Norfor-130-GF-20-NATURALE-0507.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyphenilene oxide resin, 20% glass fiber reinforced grade, good dimensional stability and thermal resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.35 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 4700 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 134 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 280 | °C | |
| Mold Temperature | 100 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® V-1 | Solvay Specialty Polymers | PPS | Ryton® |
| Monprene® CP-18126 | Teknor Apex Company | TPE | Monprene® |
| Ultramid® A3X2G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Di-Pak™ R-4912 | Hapco Inc. | TP, Unspecified | Di-Pak™ |
| MAXAMID™ PA66-NC010 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |