AKROMID® B3 GK 50 black (2311)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRP0BT_AKROMID-B3-GK-50-black-2311-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GK 50 black (2311) is a 50% glass bead reinforced polyamide 6 with low warpage and high surface appearance Applications are housings and covers in the automotive, electro and furniture industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.0 | % | |
| Water Absorption (Saturation, 23°C) | 4.7 | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.5 | % | ISO 1110 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 50 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5700 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5200 | MPa | ISO 178 |
| Flexural Stress 2 | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 1.0 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 32 | kJ/m² | |
| 23°C | 42 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 188 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Melting Temperature 3 | 225 | °C | DIN EN 11357-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Potomer SG6 | Shanghai Potomer International Trade Co., Ltd. | PVC, Unspecified | Shanghai Potomer |
| YUPLENE® R370F | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| Akulon® Ultraflow K-FHG6 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |
| Estane® 2103-90AENH TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Karina PINK COLOR CONCENTRATE 39/ 47-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |