LNP™ STAT-KON™ EX11402 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YRBzKG_LNP-STAT-KON-EX11402-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON EX11402 is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this material is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound EX11402 Product reorder name: EX11402 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.30 | g/cm³ | ASTM D792 |
| -- | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.35 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3840 | MPa | ASTM D638 |
| -- | 3730 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Fracture 2 | 74.0 | MPa | ASTM D638 |
| Fracture | 85.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Fracture 3 | 2.3 | % | ASTM D638 |
| Fracture | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 4 | 4000 | MPa | ASTM D790 |
| -- 5 | 3680 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 159 | MPa | ISO 178 |
| Fracture, 50.0mm span 6 | 132 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 16 | J/m | ASTM D256 |
| 23°C 7 | 2.3 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 350 | J/m | ASTM D4812 |
| 23°C 8 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 3.24 | J | ASTM D3763 |
| -- | 1.12 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 205 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 203 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 201 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 192 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM D696 | ||
| Flow : -30 to 30°C | 4.4E-5 | cm/cm/°C | ASTM D696 |
| Lateral : -30 to 30°C | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+5 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 - 354 | °C | |
| Middle Temperature | 354 - 366 | °C | |
| Front Temperature | 366 - 377 | °C | |
| Processing (Melt) Temp | 360 - 366 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 40 HS | RTP Company | Nylon 66 | RTP |
| Shandong Nylon A4TR01 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon, Unspecified | Shandong Nylon |
| Monprene® CP-35124 X1 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |
| Sylvin 7833-75 Red 6285 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ICORENE® 5775 | A. Schulman Europe | HDPE | ICORENE® |