TECHNYL® C 216 V35 BLACK Z
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YQpU4A_TECHNYL-C-216-V35-BLACK-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA6, reinforced with 35% of glass fibre, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183/A |
| Water Absorption (23°C, 24 hr) | 0.90 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10600 | 6900 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 195 | 115 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 2.6 | 4.0 | % | ISO 527-2/1A |
| Flexural Modulus | 10500 | 6800 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 17 | 33 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 100 | 110 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | 15 | 28 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Flow (23 to 85°C) | 2.8E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.090 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 550 | 475 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | -- | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V142-90 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| DINALON® PA 6.6 15% FV | Grupo Repol | Nylon 66 | DINALON® |
| Karina BLACK PVC COMPOUND TR-608D48/ 1-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| TABOREN® PC 62 T 50 | SILON s.r.o. | PP Copolymer | TABOREN® |
| TechnoElast V A9000 I 2 sw | TechnoCompound GmbH | TPE | TechnoElast |