China PPS hx
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YQ60CG_China-PPS-hx.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hx is newly developed toughing PPS compound which possess excellent impact resistance property as well as chemical resistance, solvent resistance, electrical insulation properties and high-temperature resistance. Its colour is ivory white. And it can be colored easily. Besides this, it can be compounded for other products. Owing to its excellent impact resistance, it can be used to make sealed parts, electrical wire and cable, automotive under-the-hood parts, lining of the fuel pipes, industrial fiber production appliances. It also can be used to make colored insulating material of electrical wire. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) | 130 | g/10 min | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 50.0 | MPa | Internal method |
| Tensile Elongation (Break) | 43 | % | Internal method |
| Flexural Modulus | 2400 | MPa | Internal method |
| Flexural Strength | 80.0 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 40 | kJ/m² | Internal method |
| Unnotched Izod Impact Strength | 140 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 285 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+17 | ohms | Internal method |
| Volume Resistivity | 2.5E+13 | ohms·cm | Internal method |
| Dielectric Strength | 18 | kV/mm | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 290 - 310 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 | °C | |
| Mold Temperature | 80.0 - 140 | °C | |
| Injection Pressure | 60.0 - 70.0 | MPa |
| Injection instructions |
|---|
| Processing time: 2 to 8hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH2801 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Kuraray Poval® PVA 420 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| Karina BLACK PVC COMPOUND 750-48/1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| KMI PP KM-4494ZW | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Sylvin 9775-70D Black | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |