RAMOFIN PPH343T8
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMOFIN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YPzgN9_RAMOFIN-PPH343T8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% MINERAL FILLED POLYPROPYLENE FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.80 to 1.2 | % | |
| -- | 0.80 to 1.2 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | |||
| Yield | 25.0 | MPa | ASTM D638 |
| Yield | 27.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 50.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 25 | J/m | ASTM D256 |
| 23°C | 16 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 142 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 85.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 168 | °C | ISO 11357-3, ASTM D3418 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 | |
| Flammability | 22 | mm/min | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 to 220 | °C | |
| Middle Temperature | 200 to 225 | °C | |
| Front Temperature | 205 to 230 | °C | |
| Mold Temperature | 30.0 to 65.0 | °C | |
| Injection Pressure | 70.0 to 105 | MPa | |
| Holding Pressure | 35.0 to 70.0 | MPa | |
| Back Pressure | 0.350 to 0.700 | MPa | |
| Screw Speed | 60 to 90 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ7400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| RheTech Polypropylene F56-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Bergamid™ B70 G30 BK801 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Grupo IDESA GPPS K-3-L-01 | Grupo IDESA, S.A. de C.V. | PS (GPPS) | Grupo IDESA GPPS |
| PC-ABSCOM™ B200 | Polymer Compounders Limited | PC+ABS | PC-ABSCOM™ |