RTP 199 X 69946
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YPFNPR_RTP199X69946.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade.
Mineral filled high gravity compound. That material can be vacuum plated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.00 | g/cm³ | ISO 1183 |
| shrinkage- Flow (4.00 mm) | 0.70 - 0.90 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 14.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 10 | % | ISO 527-2 |
| Flexural Modulus | 3200 | MPa | ISO 178 |
| Flexural Stress | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2 | 24 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 71.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3(1.5 mm, Values per RTP Company testing) | HB | ISO 1210 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 - 240 | °C | |
| Mold Temperature | 30 - 70 | °C | |
| Injection Pressure | 70.0 - 105 | MPa |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| 3 . | This rating is not intended to reflect hazards of this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PA6 A 2020/109 GF20 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Bergamid™ A700 G10 H (f1) | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Borealis PP HG313MO | Borealis AG | PP Homopolymer | Borealis PP |
| Hylon® N1033STL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| LNP™ THERMOCOMP™ PFW53U compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |