| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YNZNyA_Kingfa-PBT-UTPBT-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa PBT UTPBT-HB is a polybutene terephthalate (PBT) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main features of Kingfa PBT UTPBT-HB are:
The typical application fields of Kingfa PBT UTPBT-HB are: electrical/electronic applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 23°C | 1.3 | % | ASTM D955 |
| Transverse flow : 23°C | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 40.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 60 | % | ASTM D638 |
| Flexural Modulus 3 | 2000 | MPa | ASTM D790 |
| Flexural Strength 4 | 55.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 150 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 55.0 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Processing Temperature Limit: 270°C |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PP SC101 | Borealis AG | PP, Unspecified | Borealis PP |
| Cheng Yu T882GV1 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |
| Hifax TRC 1204X | LyondellBasell Industries | TPO (POE) | Hifax |
| Hy-Vin® XA80207 | INEOS Compounds | PVC, Flexible | Hy-Vin® |
| Karina GRAY PVC COMPOUND 450-18/363-A | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |