LNP™ LUBRICOMP™ QFL32 compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YMoC9v_LNP-LUBRICOMP-QFL32-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP QFL32 is a compound based on Nylon 6/10 containing 10% Glass Fiber, 15% PTFE. Added features of this grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound QFL-4032 Product reorder name: QFL32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 0.90 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.24 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.34 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4680 | MPa | ASTM D638 |
| -- | 4440 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 86.0 | MPa | ISO 527-2/5 |
| Break 2 | 85.0 | MPa | ASTM D638 |
| Break | 79.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 3.1 | % | ASTM D638 |
| Break | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 3850 | MPa | ASTM D790 |
| -- 5 | 3890 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 128 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 134 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.43 | ||
| vs. Itself - Static | 0.38 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 5.20 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 48.5 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 38 | J/m | ASTM D256 |
| 23°C 7 | 1.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 370 | J/m | ASTM D4812 |
| 23°C 8 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.20 | J | ASTM D3763 |
| -- | 1.50 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 196 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 189 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silopren® LSR 3786/20 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| WMB 117 | Pooya Polymer Tehran | Polyolefin, Unspecified | WMB |
| Zenite® 5130L | Celanese Corporation | LCP | Zenite® |
| Tunhe PBT TH6090 | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PBT | Tunhe PBT |
| API II ABS 920 | API II, Inc. | ABS | API II |