LNP™ VERTON™ UV00ASU compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YMVG0T_LNP-VERTON-UV00ASU-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON UV00ASU is a compound based on Polyphthalamide resin containing 50% Long Glass Fiber. Added features of this material include: UV Stabilized, Heat Stabilized, Structural. Also known as: LNP* VERTON* Compound UF-700-10 HS UV Product reorder name: UV00ASU |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.66 | g/cm³ | ISO 1183 |
| -- | 1.67 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.48 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 19300 | MPa | ASTM D638 |
| -- | 19200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 258 | MPa | ASTM D638 |
| Yield | 222 | MPa | ISO 527-2 |
| Break | 258 | MPa | ASTM D638 |
| Break | 222 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 1.8 | % | ASTM D638 |
| Yield | 1.4 | % | ISO 527-2 |
| Break | 1.8 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 17200 | MPa | ASTM D790 |
| -- | 17000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 386 | MPa | ASTM D790 |
| -- | 393 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D256 |
| 23°C 2 | 42 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 3 | 78 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 9.90 | J | ASTM D3763 |
| -- | 7.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 291 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 296 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 266 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 272 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -40 to 40°C | 1.4E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 1.5E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 to 327 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 332 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 EM | RTP Company | PC | RTP |
| RAMSTER PF302G3 | Polyram Ram-On Industries | PBT | RAMSTER |
| Gallonprene® GP420-9007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hifax TRC 134P 3004 | LyondellBasell Industries | PP Copolymer | Hifax |
| Grilamid® L XE 10987 nat | EMS-GRIVORY | Nylon 12 | Grilamid® |