Starex GC-0710
| Category: | ABS+PET , Acrylonitrile Butadiene Styrene + PET |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Starex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YMRpTP_Starex-GC-0710.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starex GC-0710 is an Acrylonitrile Butadiene Styrene + PET (ABS+PET) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: flame rated. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.44 to 0.54 | % | |
| Across Flow : 3.20 mm | 0.47 to 0.57 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 96 | ASTM D785 | |
| R-Scale | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1710 | MPa | ASTM D638 |
| -- | 2000 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 40.2 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Break | 35.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 3 | 40 | % | ASTM D638 |
| Break | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 4 | 1870 | MPa | ASTM D790 |
| -- 5 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 6 | 60.8 | MPa | ASTM D790 |
| -- 7 | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 8(23°C) | 5.2 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 270 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 120 | J/m | ASTM D256 |
| 23°C 9 | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed, 4.00 mm | 83.0 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 96.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 80.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 70.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 85.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 94.0 | °C | ISO 306/B50 |
| -- | 97.0 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yellowness Index (3.20 mm) | 25 | YI | ASTM D1925 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 | °C | |
| Desiccant Dryer | 100 | °C | |
| Drying Time | |||
| -- | 2.0 to 4.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Nozzle Temperature | 245 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 49.0 to 245 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 2.8 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Thickness: 4 mm |
| 9 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPESIN® KP212V0BLK | Kolon Plastics, Inc. | PBT | SPESIN® |
| TOTAL Polypropylene PPH 3720WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| WPP PE PE25-Black | Washington Penn Plastic Co. Inc. | MDPE | WPP PE |
| Hanwha Total PP FB53NH | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Plasmer 1045NM/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |