Braskem PE SGM9450F
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YMNwVe_BraskemPESGM9450F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description: SGM9450F is a high-density polyethylene, developed for the high molecular weight film extrusion segment produced with bimodal technology. The film produced from this resin has high tenacity and excellent resistance to impact characteristics. This resin has wide molar mass distribution that makes it easier to process. The minimum biobased content of this grade is 96%, determined according to ASTM D6866. Application: Bags in general (like T-shirt bags, Handle Bags, Star Bags, others); Geomembranes. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 9.3 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.33 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 13 µm | 40.0 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 30.0 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 85.0 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 45.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 13 µm | 590 | % | ASTM D882 |
| TD : Broken, 13 µm | 740 | % | ASTM D882 |
| Dart Drop Impact 1 | 250 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 58 | g | ASTM D1922 |
| TD : 13 µm | 51 | g | ASTM D1922 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Puncture Resistance (12.5 µm) | 80.0 | J/m | Internal method |
| Sealing Initial Temperature | 125 | °C | Internal method |
| Biobased Content | > 96 | % | ASTM D6866 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP261T | Southern Polymer, Inc. | PP Impact Copolymer | PRIMALENE |
| Moplen RP348N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Next Nylon 66 Prime Series PG40-01BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Hanwha Total PP FB72M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Sylvin 8250-70 Grey 9601 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |