PC / ABS, not Flame Retardant compound, good mechanical properties, very good impact resistance. |
General Information | |
---|---|
Features |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
Water Absorption (Saturation) | 0.15 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 2200 | MPa | ASTM D638 |
Tensile Strength (Yield) | 50.0 | MPa | ASTM D638 |
Tensile Elongation (Break) | > 100 | % | ASTM D638 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Notched Izod Impact Strength | 50 | kJ/m² | ISO 180/A |
Unnotched Izod Impact Strength | No Break | ISO 180 |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Deflection Temperature Under Load (1.8 MPa, Unannealed) | 115 | °C | ASTM D648A |
Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
RTI Elec | 80.0 | °C | UL 746 |
RTI Imp | 80.0 | °C | UL 746 |
RTI Str | 80.0 | °C | UL 746 |
Injection | Nominal Value | Unit | |
---|---|---|---|
Drying Temperature | 70.0 | °C | |
Drying Time | 3.0 | hr | |
Processing (Melt) Temp | 250 | °C | |
Mold Temperature | 60.0 | °C |
Note Message | |
---|---|
1 . | Loading 2 (50 N) |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
MTEGRITY™ PP Random Copolymer RP700 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
TOPAS® 6013F-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
Weatherflex™ CS7524WX NTL01P | Colorite Polymers | PVC, Flexible | Weatherflex™ |
APEX® 84129 | Teknor Apex Company | PVC, Flexible | APEX® |
EVALENE® HDPE HF09522 | JG Summit Petrochemical Corporation | HDPE | EVALENE® HDPE |