RheTech Polypropylene T15P100-00
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RheTech, Inc. |
| Trademark: | RheTech Polypropylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YLHESh_RheTech-Polypropylene-T15P100-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 15% Talc Reinforced Polypropylene, Natural. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 73 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 32.4 | MPa | ASTM D638 |
| Flexural Modulus | 2070 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | J/m | ASTM D256 |
| Dart Drop Impact | 0.791 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 117 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 62.8 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 - 82.2 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 193 - 221 | °C | |
| Middle Temperature | 199 - 227 | °C | |
| Front Temperature | 204 - 232 | °C | |
| Nozzle Temperature | 210 - 221 | °C | |
| Mold Temperature | 26.7 - 48.9 | °C | |
| Injection Pressure | 55.2 - 103 | MPa | |
| Holding Pressure | 27.6 - 51.7 | MPa | |
| Back Pressure | 0.345 - 1.03 | MPa |
| Injection instructions |
|---|
| Injection Speed: Variable - Application DependantScrew RPM: Recovery 3 seconds before mold opensCycle Time: Wall Thickness Dependant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® A30B02 | Polyram Ram-On Industries | Nylon 66 | Polytron® |
| Nanjing Hongrui PA66 A305 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Edgetek™ ET3200-8001 LG | PolyOne Corporation | PC | Edgetek™ |
| LNP™ THERMOCOMP™ MF006A compound | SABIC Innovative Plastics Europe | PP, Unspecified | LNP™ THERMOCOMP™ |
| Petlon Prime B1-00-00-NT | Petlon Polymers Ltd | Nylon 6 | Petlon Prime |