Petrotene® PP A3 E10 NTLA010 PH349 MSP
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YLGUsA_Petrotene-PP-A3-E10-NTLA010-PH349-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The impact modified polypropylene for injection molding with good set of mechanical properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 to 0.990 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 2.0 to 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 14.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 200 | % | ASTM D638 |
| Flexural Modulus | 600 | MPa | ASTM D790 |
| Flexural Strength | 15.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Continuous Use Temperature | 90.0 | °C | |
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TORZEN® T2000HSL BK20 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| ChronoPrene™ 25A | CardioTech International, Inc. | TPE | ChronoPrene™ |
| Elastron® V V101.A65.N | Elastron USA, Inc. | TPV | Elastron® V |
| LNP™ LUBRICOMP™ ICL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |
| Lupol® HM5204 | LG Chem Ltd. | TPO | Lupol® |