Generic PPS - Glass\Mineral
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKfuLB_Generic-PPS---Glass-Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PPS - Glass\Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.79 - 2.00 | g/cm³ | ASTM D792 |
| 23°C | 1.81 - 2.00 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.15 - 0.31 | % | ASTM D955 |
| Transverse flow : 23°C | 0.38 - 1.0 | % | ASTM D955 |
| 23°C | 0.14 - 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.020 - 0.025 | % | ASTM D570 |
| 23°C, 24 hr | 0.019 - 0.020 | % | ISO 62 |
| Saturated, 23°C | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 99 - 122 | ASTM D785 | |
| 23°C | 97 - 124 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 14200 - 19100 | MPa | ASTM D638 |
| 23°C | 10600 - 23000 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 129 - 173 | MPa | ISO 527-2 |
| Fracture, 23°C | 110 - 165 | MPa | ASTM D638 |
| Fracture, 23°C | 50.0 - 167 | MPa | ISO 527-2 |
| 23°C | 100 - 174 | MPa | ASTM D638 |
| 23°C | 113 - 172 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 0.50 - 2.1 | % | ASTM D638 |
| Fracture, 23°C | 0.43 - 1.8 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 12800 - 20100 | MPa | ASTM D790 |
| 23°C | 10700 - 22100 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 172 - 261 | MPa | ASTM D790 |
| 23°C | 126 - 262 | MPa | ISO 178 |
| Compressive Strength (23°C) | 138 - 295 | MPa | ASTM D695 |
| Shear Strength (23°C) | 60.0 - 65.6 | MPa | ASTM D732 |
| Poisson's Ratio (23°C) | 0.34 - 0.36 | ASTM E132 | |
| Coefficient of Friction | 0.30 - 0.35 | ASTM D1894 | |
| Taber Abrasion Resistance (23°C) | 70.0 - 70.8 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.9 - 9.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 5.3 - 31 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 38 - 100 | J/m | ASTM D256 |
| 23°C | 5.9 - 7.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 200 - 320 | J/m | ASTM D256 |
| 23°C | 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 259 - 270 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 259 - 276 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 215 - 220 | °C | ISO 75-2/C |
| Melting Temperature | 278 - 280 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 4.0E-6 - 2.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.0E-5 - 1.5E-5 | cm/cm/°C | ASTM E831 |
| Flow | 9.6E-6 - 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.7E-5 - 4.8E-5 | cm/cm/°C | ASTM D696 |
| Lateral | 3.0E-5 - 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 1.9E-5 - 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+3 - 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | |||
| 23°C | 5.5E+2 - 2.5E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+2 - 1.3E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 11 - 18 | kV/mm | ASTM D149 |
| 23°C | 13 - 26 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 23°C | 3.78 - 5.04 | ASTM D150 | |
| 23°C | 3.97 - 5.85 | IEC 60250 | |
| 23°C | 5.15 | IEC 60250 | |
| Dissipation Factor | |||
| 23°C | 8.0E-4 - 9.2E-3 | ASTM D150 | |
| 23°C | 1.0E-3 - 2.1E-3 | IEC 60250 | |
| Arc Resistance | 180 - 186 | sec | ASTM D495 |
| Comparative Tracking Index | 146 - 227 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 119 - 143 | °C | |
| Drying Time | 3.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.020 - 0.052 | % | |
| Rear Temperature | 280 - 321 | °C | |
| Middle Temperature | 310 - 330 | °C | |
| Front Temperature | 310 - 335 | °C | |
| Nozzle Temperature | 305 - 320 | °C | |
| Processing (Melt) Temp | 326 - 335 | °C | |
| Mold Temperature | 134 - 151 | °C | |
| Injection Pressure | 75.0 - 75.6 | MPa | |
| Holding Pressure | 49.9 - 50.0 | MPa | |
| Back Pressure | 0.345 - 1.61 | MPa | |
| Screw Speed | 50 - 125 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PPS - Glass\MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tarnamid® T- 30 MCS | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Texalan® 3 Series 365A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| Ultramid® 8255 HS | BASF Corporation | Nylon 6 | Ultramid® |
| Geon™ Vinyl Rigid Extrusion 87548 AS | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Karina IVORY PVC COMPOUND 105950-35/1-AY-IS-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |