Sumikon® PM-9630 (Type: JT Black)
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKYbKh_SumikonPM9630TypeJTBlack.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® PM-9630 (Type JT Black) is Glass fiber and Inorganic filler filled resol resin (non-anmonia phenolic) molding compound with good electronic property and heat resistance. This grade is official registered UL with V-0 (t=0.16). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.77 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.16 | % | JIS K6911 |
| Water Absorption (Equilibrium) | 0.090 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 137 | MPa | JIS K6911 |
| Flexural Modulus | 14600 | MPa | JIS K6911 |
| Flexural Strength | 208 | MPa | JIS K6911 |
| Compressive Strength | 208 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.4 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 9.0 | kV/mm | JIS K6911 |
| Arc Resistance | 179 | sec | JIS K6911 |
| Insulation Resistance | JIS K6911 | ||
| -- 2 | 4.0E+12 | ohms | JIS K6911 |
| -- 3 | 1.0E+12 | ohms | JIS K6911 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.160 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B (step by step) |
| 2 . | As molded |
| 3 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 803 GB 20 TFE 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| Spartech Polycom M60155 | Spartech Polycom | PVC Alloy | Spartech |
| WELLAMID Nylon 6000 GS 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| ARC ARC60G33 | ARC Resin Corporation | Nylon 6 | ARC |
| LNP™ THERMOCOMP™ RC003SXS compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ THERMOCOMP™ |