SABIC® PPcompound G3240U
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YKG2Vg_SABIC-PPcompound-G3240U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® PPCOMPOUND G3240U is a general purpose, 40% glass filled, chemically coupled, heat stabilized and UV stabilized homopolymer polypropylene compound. The IMDS ID is 209768078. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 23°C, 48 hr | 0.80 | % | |
| Flow : 23°C, 48 hr | 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7610 | MPa | ASTM D638 |
| -- | 8900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 120 | MPa | ASTM D638 |
| Break | 111 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Break 3 | 2.4 | % | ASTM D638 |
| Break | 2.9 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 64.0 mm Span 4 | 8900 | MPa | ISO 178 |
| 50.0 mm Span 5 | 7810 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 6 | 13 | kJ/m² | |
| 23°C 7 | 10 | kJ/m² | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm 8 | 98 | J/m | ASTM D256 |
| -30°C 9 | 11 | kJ/m² | ISO 180/1A |
| 23°C 10 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact 11(23°C, 3.20 mm) | 610 | J/m | ASTM D4812 |
| Instrumented Dart Impact 12(23°C, Energy at Peak Load) | 4.34 | J | ASTM D3763 |
| Gardner Impact 13(23°C) | 0.380 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 161 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 14 | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 153 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 15 | 153 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 164 | °C | ISO 306/A50 |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 16.7 | µm/Mk | |
| Transverse : -30 to 100°C | 155 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4mm, Cut |
| 7 . | 80*10*4 mm, Cut |
| 8 . | 63.5*12.7*3.2mm, Cut |
| 9 . | 80*10*4mm, Cut |
| 10 . | 80*10*4mm, Cut |
| 11 . | 63.5*12.7*3.2mm, Cut |
| 12 . | 2.20 m/sec |
| 13 . | 0.625"d tup |
| 14 . | 80*10*4mm, Cut |
| 15 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VITAMIDE® BF23YL6634 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| TOTAL Polypropylene PPH 10012 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| INSTRUC PPGF20CC | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |
| Latilub 75/4-05T G/30-V0 | LATI S.p.A. | PBT | Latilub |
| Karina CLEAR PVC COMPOUND 65/229-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |