Latilon 30D-V0
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YIfgq7_Latilon-30D-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate (PC) based compound. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE and antimonium trioxide free. Low smoke density and low toxicity index. Very high dimensional stability. Very good surface appearance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.60 to 0.75 | % | |
| Flow : 2.00 mm | 0.55 to 0.75 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2500 | MPa | |
| 60°C | 2200 | MPa | |
| 90°C | 1900 | MPa | |
| 120°C | 1700 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 70.0 | MPa | |
| Yield, 60°C | 60.0 | MPa | |
| Yield, 90°C | 55.0 | MPa | |
| Yield, 120°C | 40.0 | MPa | |
| Break, 23°C | 55.0 | MPa | |
| Break, 60°C | 35.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 8.0 | % | |
| Yield, 60°C | 6.0 | % | |
| Yield, 90°C | 4.0 | % | |
| Yield, 120°C | 2.5 | % | |
| Break, 23°C | 80 | % | |
| Break, 60°C | 70 | % | |
| Break, 90°C | > 100 | % | |
| Break, 120°C | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 140 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Oxygen Index | 36 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Regrind | 15 | % | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NatureFlex™ 30NVR | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| DESOX™ DSC401GMW5 | DESCO Co., Ltd. | PBT | DESOX™ |
| HiFill® PEEK CF15 A | Techmer Engineered Solutions | PEEK | HiFill® |
| Jampilen EP548S | Jam Polypropylene Company | PP Copolymer | Jampilen |