LNP™ STAT-LOY™ K3000Z compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YIL2Zc_LNP-STAT-LOY-K3000Z-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY K3000Z is a compound based on unfilled Acetal resin. Added feature of this material is: Antistat. Also known as: LNP* STAT-LOY* Compound K-E Product reorder name: K3000Z |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.32 | g/cm³ | ASTM D792 |
| -- | 1.33 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.8 | % | |
| Across Flow : 24 hr | 1.8 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 2.3 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 4.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1600 | MPa | ASTM D638 |
| -- | 1500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 41.8 | MPa | ASTM D638 |
| Yield | 42.0 | MPa | ISO 527-2 |
| Break | 32.3 | MPa | ASTM D638 |
| Break | 36.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 16 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2 |
| Break | 60 | % | ASTM D638 |
| Break | 49 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1440 | MPa | ASTM D790 |
| -- | 1500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 49.0 | MPa | ASTM D790 |
| -- | 40.1 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.25 | ||
| Wear Factor - Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | No Break | ASTM D256 | |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 28.8 | J | ASTM D3763 |
| -- | 16.7 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 67.8 | °C | |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.3E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 193 to 204 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LPT381 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Moplen EP439S | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| Taitacell EPS 301MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Alathon® L5840 | LyondellBasell Industries | HDPE | Alathon® |
| DENISTAT N 00U 03 | Vamp Tech | Nylon 6 | DENISTAT |