A tough, rubber-like urethane compound for making a broad range of repairs to protect against wear, abrasion, and noise reduction.

Intended Use:

Protect equipment surfaces from wear and abrasion.

Protect processing equipment such as coating hoppers, lining chutes, pump volutes, impellers, and fan housings.

Product features:

Excellent tear resistance

Mixes easily

Bonds (with primers) to metal, concrete, rubber, wood, and fiberglass

Highly resistant to impact and abrasion

Trowels on smoothly

General Information
Features	Impact resistance, high Good tear strength Good wear resistance Good toughness
Uses	Repair Materials
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Specific Volume	0.849	cm³/g
Solid content- by Volume	88	%

Mechanical	Nominal Value	Unit	Test Method
Abrasion Loss	140	mg/1000 cycles

Thermal	Nominal Value	Unit
Maximum Operating Temperature
Dry	82	°C
Wet	49	°C

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	12	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	78		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength	31.0	MPa	ASTM D412
Tensile Elongation (Break)	600	%	ASTM D412
Tear Strength	70.1	kN/m	ASTM D624

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	14	kV/mm	ASTM D149

Thermoset	Nominal Value	Unit
Thermoset Components
Resin	Mixing ratio by weight: 94
Hardening method	Mixing ratio by weight: 6.0
Pot Life (24°C)	10	min
Demold Time	600	min

Additional Information
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit
Curing Time	16	hr

Resin Grade	Manufacturer	Category	Trademark
ADENE NHJAGD	A.D. Compound spa	PP Copolymer	ADENE
BESTNYL SE15VI01A	Triesa Plastics	Nylon 66	BESTNYL
Hostalen PP H5416 K	LyondellBasell Industries	PP Random Copolymer	Hostalen
CP PRYME® Nylon 66 NN213HSL BK/OM200	Chase Plastics Services Inc.	Nylon 66	CP PRYME® Nylon 66
ALTECH® PA66 ECO 1000/617	ALBIS PLASTIC GmbH	Nylon 66	ALTECH® PA66