LUBLENE GK40 NATURAL
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBLENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGY15E_LUBLENE-GK40-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on PP first choice natural. With glass beads 40%. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 to 1.24 | g/cm³ | ISO 1183/A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 to 3200 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/5 | ||
| Yield | 25.0 to 30.0 | MPa | |
| Break | 20.0 to 25.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/5 | ||
| Yield | 4.0 to 5.0 | % | |
| Break | 25 to 30 | % | |
| Flexural Modulus 1 | 1700 to 2700 | MPa | ISO 178 |
| Flexural Stress 2 | 35.0 to 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 to 4.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 25 to 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 30 to 40 | J/m | ASTM D256A |
| 23°C 3 | 25 to 35 | kJ/m² | ASTM D256 |
| 23°C | 3.5 to 4.5 | kJ/m² | ISO 180/A |
| 23°C 4 | 3.0 to 4.0 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | 25 to 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 120 to 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 125 to 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 60.0 to 70.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 100 to 110 | °C | ISO 306/A120 |
| -- | 95.0 to 105 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-201-G25 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| VALOX™ ENH8530 resin | SABIC Innovative Plastics Europe | PBT+PET | VALOX™ |
| ACCUTECH™ HP0336T20L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Haysite Plastics EHC | Haysite Reinforced Plastics | Polyester, TS | Haysite Plastics |
| LG PMMA ID158 | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |