ACRYPET® IR G304
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Mitsubishi Rayon Co., Ltd. |
| Trademark: | ACRYPET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGWwXR_ACRYPET-IR-G304.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Acrypet®IR G304 is a polymethyl methacrylate-acrylic material,. This product is available in North America,. Acrypet®The main characteristics of IR G304 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.2 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 55.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 78 | % | ASTM D638 |
| Flexural Modulus (6.35 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength (6.35 mm) | 78.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 38 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 109 | °C | ASTM D1525 |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (3200 µm) | 92.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Surface Resistivity, JIS K6911: >10^16 ohmVolume Resistivity, JIS K6911: >10^15 ohm-cmDielectric Breakdown Strength: 18 kV/mmDielectric Constant, 60Hz: 3.9Dielectric Loss Tangent, 60Hz: 0.04Arc Resistance, JIS K6911: No Trace |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PVC Film 06-A0370R-80 NT | Teknor Apex Company | PVC, Flexible | PVC Film |
| SUPREME GPPS SC202LV | Supreme Petrochem Ltd. | PS (GPPS) | SUPREME GPPS |
| Surlyn® 2601 | DuPont Packaging & Industrial Polymers | Ionomer | Surlyn® |
| BUP 640 | Bonyan Kala Chemie Company | Polyester, TS | BUP |
| DuPure® L 76 A | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |