WPP PP PPC3TF1.3-Natural
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGTpYH_WPP-PP-PPC3TF1-3-Natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PPC3TF1.3-Natural is a polypropylene copolymer (PP Copoly) product, which contains 13% talc filler. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.990 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 35.0 | MPa | ASTM D638 |
| Yield | 36.0 | MPa | ISO 527-2/50 |
| Flexural Modulus | |||
| Tangent 2 | 2100 | MPa | ASTM D790 |
| -- 3 | 2200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 29 | J/m | ASTM D256 |
| -40°C | 2.0 | kJ/m² | ISO 180 |
| -15°C | 2.1 | kJ/m² | ISO 180 |
| 23°C | 3.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 127 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 119 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.0 | °C | ISO 75-2/A |
| Additional Information |
|---|
| Tested at 23 ± 2°C (73.4 ± 3.6°F) and 50 ± 5% relative humidity unless otherwise noted |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostacom EYC 186N Black | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lucobit 1210A | Lucobit AG | PE Copolymer | Lucobit |
| OnForce™ LFT LFT PP-30 LGF/000 1001 | PolyOne Corporation | PP Homopolymer | OnForce™ LFT |
| 3M™ Dyneon™ Fluoroelastomer FE 5624Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Sylvin 2976-80 White 1500 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |