SITRALON 18E-TF10-HK / C7043 Dark Grey
| Category: | PC , Polycarbonate |
| Manufacturer: | SITRAPLAS GmbH |
| Trademark: | SITRALON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YGIXMH_SITRALON-18E-TF10-HK-C7043-Dark-Grey.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 18.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 58.0 | MPa | ISO 527-2/50 |
| Break | 50.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66/6 GF 30 FRG 5 TS | Plastcom | Nylon 66/6 | SLOVAMID® 66/6 |
| Aaroprene® TFIPP 2010 | Aaron Industries Corp. | PP, Unspecified | Aaroprene® |
| Bionolle™ 1020 MD | Showa Denko K.K. | Biodeg Polymers | Bionolle™ |
| ELASTOSIL® P 7616-195 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| Karina BLACK PVC COMPOUND 681D48/11-CY-ISI-SD (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |