Hostaform® SXT90Z-01 XAP
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Hostaform® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YEvT79_Hostaform-SXT90Z-01-XAP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostaform® acetal copolymer grade SXT90Z-01 XAP is UV stabilized, impact modified material available in a range of colors for automotive interior applications plus meets the typical low emission requirements of the automotive market. Chemical abbreviation according to ISO 1043-1: POM-HI Low emission performance (VDA 275) < 10 ppm |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Water Absorption (Saturation, 23°C) | 0.65 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 49.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 12 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 166 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 180 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 60.0 - 70.0 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Zone 4 Temperature: 180 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 2500 | POLY GIN | PC | MARCOBLEND |
| Royalite R72 | Spartech Plastics | PMMA+PVC | Royalite |
| Tenite™ Propionate 380A3V32818 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Hydrin® T5010 | Zeon Chemicals L.P. | Epoxy | Hydrin® |
| Karina CLEAR PVC COMPOUND 800/202-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |