LNP™ STAT-LOY™ M3000 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YEtUrX_LNP-STAT-LOY-M3000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-LOY* M3000 is a compound based on unfilled Polypropylene resin. Added feature of this material is: Antistat. Also known as: LNP* STAT-LOY* Compound M Product reorder name: M3000 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.950 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 1.4 | % | |
| Across Flow : 24 hr | 1.3 | % | |
| Water Absorption (24 hr, 50% RH) | 0.85 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1390 | MPa | ASTM D638 |
| -- | 1350 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 28.6 | MPa | ASTM D638, ISO 527-2 |
| Break | 18.4 | MPa | ASTM D638 |
| Break | 7.84 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.6 | % | ASTM D638 |
| Yield | 8.1 | % | ISO 527-2 |
| Break | 47 | % | ASTM D638 |
| Break | 98 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 1450 | MPa | ASTM D790 |
| -- | 1360 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 40.7 | MPa | ASTM D790 |
| -- | 32.2 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 9.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D4812, ISO 180/1U | |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.94 | J | ASTM D3763 |
| -- | 5.77 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 3 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 56.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 59.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 to 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 to 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 199 to 210 | °C | |
| Processing (Melt) Temp | 188 to 199 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Styrolution PS 3100/3101 | INEOS Styrolution Group GmbH | PS (GPPS) | Styrolution PS |
| BIPEX B0620FN | Ginar Technology Co., LTD. | PBT | BIPEX |
| Celstran® PP-GF30-0553 Black | Celanese Corporation | PP Copolymer | Celstran® |
| Osterlene® LLM1018SA | Osterman & Company | LLDPE | Osterlene® |
| 3M™ Dyneon™ Fluoroelastomer FE 5610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |