Chemlon® MDF606 Datasheet,Nylon 6,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
MDF606 is a 30% glass fibre reinforced, impact modified nylon 6 that offers good rigidity and toughness over a wide temperature range. The grade is also stabilised for good weathering performance in outdoor applications.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	Impact modifier
Features	Impact modification Good weather resistance Thermal stability, good Good toughness Medium hardness
Uses	Outdoor application
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.30	g/cm³	ISO 1183
Molding Shrinkage ¹	0.70 - 1.4	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.8	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	120	MPa	ISO 527-2
Tensile Strain (Break)	6.0	%	ISO 527-2
Flexural Modulus	6700	MPa	ISO 178
Flexural Stress ²	165	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	18	kJ/m²	ISO 179
Notched Izod Impact	14	kJ/m²	ISO 180

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	°C	ISO 75-2/B
1.8 MPa, not annealed	> 190	°C	ISO 75-2/A

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm, Teknor Apex test result)	HB		UL 94
Oxygen Index	22	%	ISO 4589-2

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	2.0	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	< 300	°C
Mold Temperature	60.0 - 80.0	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
Back pressure: LowInjection pressure: HighNo drying is necessary unless the materials has been exposed to air for longer than three hours.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).
2 .	At conventional deflection

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

2 .

At conventional deflection

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YDWGNG_Chemlon-MDF606.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 2583C HEC FR	RTP Company	PC+ABS	RTP
Spartech Polycom SPF7015A	Spartech Polycom	PC	Spartech
ALFATER XL® D40E 2GP0000	ALBIS PLASTIC GmbH	TPV	ALFATER XL®
COSMOPLENE® FL7641L	TPC, The Polyolefin Company (Singapore) Pte Ltd	PP, Unspecified	COSMOPLENE®
LNP™ THERMOCOMP™ EC008APQ compound	SABIC Innovative Plastics	PEI	LNP™ THERMOCOMP™