PALMID® R 6 S
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | pal plast GmbH |
| Trademark: | PALMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YD2hnr_PALMID-R-6-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PALMID®R 6 S is a polyamide 6 (nylon 6) product,. It can be processed by injection molding and is available in Europe. Typical application areas are: engineering/industrial accessories. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 8.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.9 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, 23°C) | 82.5 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break (23°C) | 25 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 202 | °C | ISO 306/B50 |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| Tensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 3000 to 3200 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 80 to 85 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 3 to 5 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: 20 to 30 %Charpy Notched Impact, ISO 179, Type 1, Edgewise, Notch A, 23°C: 6 to 9 kJ/m²Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 200 to 204 °CDensity, ISO 1183: 1.12 to 1.14 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 8 to 9 %Moisture Absorption, ISO 62, 23°C, 50% RH: 2.8 to 3 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® F5A EX | Solvay Specialty Polymers | PTFE | Polymist® |
| Vistalon™ 8600 | ExxonMobil Chemical | EPDM | Vistalon™ |
| ACCUTECH™ CP0437T40V | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| Borealis PP BD020AIB | Borealis AG | PP, Unspecified | Borealis PP |
| KMI PP KM-0275ZW | KMI Group, Inc. | PP Impact Copolymer | KMI PP |