Alathon® M5370
| Category: | HDPE Copolymer , High Density Polyethylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YB7O7x_Alathon-M5370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Alathon M5370 is a copolymer with a narrow molecular weight distribution. This resin provides high impact strength, excellent color, low odor and good processing stability. Typical applications include open head pails and large shipping containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.53 to 0.59 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.9 | g/10 min | ASTM D1238 |
| Spiral Flow | 22.6 | cm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 71 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 1040 | MPa | |
| 1% Secant | 823 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 28.5 | MPa | |
| Break | 20.6 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 9.0 | % | |
| Break | 1200 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1410 | MPa | |
| 1% Secant | 1300 | MPa | |
| 2% Secant | 1090 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 72.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 130 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 117 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ E 103 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Sindustris PP HM3103A | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| NOVADURAN® 5308F20 | Mitsubishi Engineering-Plastics Corp | PBT Alloy | NOVADURAN® |
| 3M™ Dyneon™ PTFE Compound TF 8615 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Jamplast JPPPO | Jamplast, Inc. | PPE+PS | Jamplast |