Epoxies, Ect. 20-2370
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Epoxies, Etc. |
| Trademark: | Epoxies, Ect. |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YAsdgi_Epoxies-Ect-20-2370.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This two component urethane series are low durometer (30-90 Shore A), potting, casting, and encapsulating compounds. They are unfilled materials engineered to provide excellent hydrolytic stability and low moisture permeability. They have outstanding thermal cycling properties, low glass transition temperatures and low embedment stress to sensitive electronic components. These unique urethane formulations maintain their integrity over a wide operating temperature range. The low glass transition temperature of approximately -70°C makes these urethanes ideal for low temperature potting applications. These systems exhibit very little hardness increase when cooled to -72°C. Features:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature | -70.0 | °C | |
| CLTE - Flow | 2.3E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity (25°C) | 4300 | cP |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | -40.0 to 125 | °C |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Black | ||
| Mix Ratio by Weight (PBW) | |||
| Part A | 100 | ||
| Part B | 25 | ||
| Density | |||
| 25°C 1 | 0.898 | g/cm³ | |
| 25°C 2 | 1.20 | g/cm³ | |
| Curing Time | |||
| 85°C | 0.66 | hr | |
| 65°C | 1.5 | hr | |
| 45°C | 2.5 | hr | |
| 25°C | 24 to 48 | hr | |
| Pot Life 3(25°C) | 60 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 70 | ||
| Tensile Strength | 5.69 | MPa | |
| Tensile Elongation at Break | 250 | % | |
| Relative Permittivity (1 kHz, 25°C) | 4.50 | ||
| Volume Resistivity | 6.0E+16 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 100 gram mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOPLAST 135 FT EB | Zylog Plastalloys | TPV | NEOPLAST |
| Aaroprene® ATPR 1000 60A | Aaron Industries Corp. | TPE | Aaroprene® |
| LNP™ THERMOCOMP™ RX96592 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| EPAMOULD 650D12 | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| NORYL GTX™ GTX830 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |