Order Products : sales@su-jiao.com
RONFALIN® ABS 1220 MW 20 U
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | A. Schulman Europe |
| Trademark: | RONFALIN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y9k7K6_RONFALINABS1220MW20U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Wollastonite mineral filled ABS compound, UV stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 4.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 96.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 33.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 39 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 81.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification (1.6 mm) | HB | IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Regrind | 30 | % | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 40 - 80 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP648V | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| GLAMIDE® T-222SA | TOYOBO America, Inc. | Nylon 6 Elast | GLAMIDE® |
| K-Resin® SBC KR03NW | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |
| LNP™ THERMOCOMP™ IX04513C compound | SABIC Innovative Plastics | Nylon 612 | LNP™ THERMOCOMP™ |
| Paracril® BJ | INSA | NBR | Paracril® |