Hyundai EP Adhesives LE200T/1002
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP Adhesives |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y9efqf_Hyundai-EP-Adhesives-LE200T-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP Adhesives LE200T/1002 is a Polyethylene product. It is available in Asia Pacific. Applications of Hyundai EP Adhesives LE200T/1002 include adhesives/tapes and coating applications. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.927 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 47 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 17.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion Strength | > 3.4 | kN/m | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 528K | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| Tenite™ Propionate 360A4861307 Clear, Trsp | Eastman Chemical Company | CAP | Tenite™ Propionate |
| Nypol® PA B3 HS BLACK NT378 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| LubriOne™ NN-30GF/10T WHT | PolyOne Corporation | Nylon 66 | LubriOne™ |
| Polifor® QD 813 Y001 NATURALE WOD | SO.F.TER. SPA | PP Copolymer | Polifor® |