Panlite® EN-8615N
| Category: | PC , Polycarbonate |
| Manufacturer: | TEIJIN LIMITED |
| Trademark: | Panlite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y6qsvo_Panlite-EN-8615N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EMI shield (Phosphor type flame resistance) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 4.00 mm | 0.28 to 0.48 | % | |
| Flow : 4.00 mm | 0.070 to 0.27 | % | |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7600 | MPa | ISO 178 |
| Flexural Stress 2 | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 8.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 22 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 118 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 110 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 124 | °C | ISO 306/B50 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.0E-5 | cm/cm/°C | |
| Transverse | 8.0E-5 | cm/cm/°C | |
| RTI Elec (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Imp (1.50 mm) | 80.0 | °C | UL 746 |
| RTI Str (1.50 mm) | 80.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 6.0 | ohms | IEC 60093 |
| Volume Resistivity | 0.50 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200D L | RTP Company | Nylon 612 | RTP |
| Wellamid® GF1750-BK2 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Hetron™ FR 650 T-20 | Ashland Performance Materials | Polyester, TS | Hetron™ |
| PLUSTEK RA502 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| Osterlene® HM0550 | Osterman & Company | HDPE, HMW | Osterlene® |