Stratasys PC-ABS
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Stratasys |
| Trademark: | Stratasys |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y6Z0Ma_Stratasys-PC-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Production-Grade Thermoplastic for Fortus 3D Production Systems PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-ABS offers the most desirable properties of both materials - the superior strength and heat resistance of PC and the flexibility of ABS. PC-ABS blends are commonly used in automotive, electronics and telecommunications applications. Additionally, a PC-ABS part manufactured on a Fortus® 3D Production System is 5-60 percent stronger than a part made on previous FDM® systems. When combined with a Fortus system, PC-ABS gives you Real Parts™ conceptual modeling, functional prototyping, manufacturing tools, and end-use-parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Thickness - Layer Capability | 127.0 to 330.2 | µm |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistance 1 | 4.4E+13 to 2.0E+14 | ohms | ASTM D257 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(3.18 mm) | 1920 | MPa | ASTM D638 |
| Tensile Strength 3(3.18 mm) | 40.7 | MPa | ASTM D638 |
| Tensile Elongation 4(Break, 3.18 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 5 | 1930 | MPa | ASTM D790 |
| Flexural Strength 6 | 67.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 200 | J/m | ASTM D256A |
| Unnotched Izod Impact (23°C) | 480 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 110 | °C | |
| 1.8 MPa, Unannealed | 96.1 | °C | |
| Glass Transition Temperature | 125 | °C | DMA |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 |
| CLTE - Flow | 7.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 3.5 to 13 | kV/mm | ASTM D149 |
| Dielectric Constant 7 | 2.70 to 2.90 | ASTM D150 | |
| Dissipation Factor 8 | 3.2E-3 to 3.5E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | Type I, 5.1 mm/min |
| 5 . | Method I (3 point load), 1.3 mm/min |
| 6 . | Method I (3 point load), 1.3 mm/min |
| 7 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| 8 . | All Electrical Property values were generated from the average of test plaques built with default part density (solid). Test plaques were 4.0 x 4.0 x 0.1 inches (102 x 102 x 2.5 mm) and were built both in the flat and vertical orientation. The range of values is mostly the result of the difference in properties of test plaques built in the flat vs. vertical orientation. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Acetate 105E4T62328 Natural, Trsp | Eastman Chemical Company | CA | Tenite™ Acetate |
| AKROMID® B3 GF 60 1 natural (2468) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Chiao Fu PA6 MC212STG20 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 6 | Chiao Fu PA6 |
| LEXAN™ CFR5630D resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Sylvin 4240-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |