Staramide RF00ASXP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y5wHpA_Staramide-RF00ASXP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide RF00ASXP is a 50 % Glass Fiber Reinforced Polyamide 66 Injection Molding Resin heat stabilized (also known as Staramide 66 G 50V S3) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 0.10 to 0.30 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 210 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 14100 | MPa | ISO 178 |
| Flexural Stress | 305 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 2(23°C) | 15 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 80 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 259 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 246 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.6E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 8.4E-5 | cm/cm/°C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrathane™ ALC-85A-B20 | Biomerics, LLC | TPU-PC | Quadrathane™ |
| ELASTOSIL® P 7950 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® P |
| LOXIM 330 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |
| ALTECH® PP-H A 2030/169 GF30 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Sylvin 7833-85 Red 6300 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |