RIALFILL H 15 S 20 MJ
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y40z4S_RIALFILL-H-15-S-20-MJ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ppolypropylene homopolymer compound 20% mica reinforced with thermal stabilization of process Product specific for injection molding of article with high rigidity and thermo-resistance, low dimensional shrinkage and low linear thermal coefficient. Available in natural version and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 1.1 | % | ISO 294-4 |
| Flow direction | 0.95 | % | ISO 294-4 |
| Water Absorption 1(23°C, 24 hr) | 0.030 | % | ISO 62 |
| Ash Content | 20 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 4.2 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 75 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 31.0 | MPa | ISO 527-2/20 |
| Fracture, 23°C | 27.0 | MPa | ISO 527-2/20 |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 5.0 | % | ISO 527-2/20 |
| Fracture, 23°C | 10 | % | ISO 527-2/20 |
| Flexural Modulus 2(23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 48.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 27 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | ISO 180/1A | ||
| -20°C | 1.8 | kJ/m² | ISO 180/1A |
| 23°C | 2.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 124 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 97.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 - 220 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flex® TPE A8030 | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Bynel® 50E806 | DuPont Packaging & Industrial Polymers | PP, Unspecified | Bynel® |
| Cheng Yu N6GV25 | Cheng Yu Plastic Company Limited | Nylon 6 | Cheng Yu |
| Xytron™ M6510A | DSM Engineering Plastics | PPS | Xytron™ |
| Sylvin 4250-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |