Lexan* 955 Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant PC has an UL-94 V0 rating and is available in various opaque color options. Lexan 955 resin is of high viscosity for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.80 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2280 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 62.1 | MPa | ASTM D638 |
| Fracture | 65.5 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 6.4 | % | ASTM D638 |
| Fracture | 130 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2340 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 101 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 73.4 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 127 | °C | ASTM D648 |
| Vicat Softening Temperature | 143 | °C | ASTM D1525 6 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance 7 | PLC 7 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 3 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-2 | UL 94 | |
| 1.5 mm | V-0 | UL 94 | |
| 3.1 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index (1.0 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.0 mm) | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 288 - 310 | °C | |
| Middle Temperature | 299 - 321 | °C | |
| Front Temperature | 310 - 332 | °C | |
| Nozzle Temperature | 304 - 327 | °C | |
| Processing (Melt) Temp | 310 - 332 | °C | |
| Mold Temperature | 82 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| 7 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALENE® P 100 SGF20 ST F V-0 natural | RIA-Polymers GmbH | PP, Unspecified | RIALENE® |
| CERTENE™ PBM-12 | Muehlstein | PP Impact Copolymer | CERTENE™ |
| Duron PPE/PA 820 | ProPolymers Inc. | Nylon+PPE | Duron |
| Hostaform® MT12U03 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Karina IVORY PVC COMPOUND -E 853-35/ 1-DY-IS(AS-80)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |