Fiberfil® J-60/30
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Fiberfil® Engineered Plastics Inc. |
| Trademark: | Fiberfil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y3nqGy_Fiberfil-J-60-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Fiberfil®J-60/30 is a polypropylene homopolymer (PP Homopoly) material, and the filler is 30% glass fiber reinforced material. This product is available in North America,. Fiberfil®The main characteristics of J-60/30 are: homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | ||
| 3.18 mm | 0.30 | % | ASTM D955 |
| 6.35 mm | 0.40 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5860 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 65.5 | MPa | ASTM D638 |
| Tensile Elongation (Yield, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent (23°C) | 4830 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 149 | °C | ASTM D648 |
| Additional Information |
|---|
| Rockwell Hardness, ASTM D785, R-Scale: 100 to 110 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 10756 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Leona™ WG143 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Lucel® HI510 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucel® |
| LUVOCOM® 20-8565 | Lehmann & Voss & Co. | PPA | LUVOCOM® |
| Dow Corning® QP1-240 | Dow Corning Corporation | Silicone | Dow Corning® |