POLYfill PPC GF5020
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYfill |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y2PSmG_POLYfill-PPC-GF5020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fibre-reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 30.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2500 | MPa | ISO 178 |
| Flexural Stress | 46.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 129 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 96.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 138 | °C | ISO 306/A50 |
| -- | 79.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polytron® P60B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| RONFALIN® FF50 | A. Schulman Europe | ABS | RONFALIN® |
| Desmopan® DP 2590A | Covestro - PUR | TPU-Polyester | Desmopan® |
| InnoClear™ VA-273 | Innovative Polymers, Inc. | TSU | InnoClear™ |
| Karina WHITE PVC COMPOUND 850-10/116-Y-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |