RTP EMI 2262
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1yUrB_RTP-EMI-2262.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm, Injection Molded) | 1.0 - 1.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.18 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 3510 | MPa | ASTM D638 |
| Tensile Strength | 83.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield, Injection Molded) | 4.0 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 3580 | MPa | ASTM D790 |
| Flexural Strength (Injection Molded) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm, Injection Molded) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 210 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Injection Molded) | 171 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0 | ohms·cm | ASTM D257 |
| Additional Information |
|---|
| Static Decay MIL-PRF-81705D, FTMS-4046.1: <2 sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 343 - 388 | °C | |
| Middle Temperature | 343 - 388 | °C | |
| Front Temperature | 343 - 388 | °C | |
| Mold Temperature | 163 - 218 | °C | |
| Injection Pressure | 69.0 - 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Amilan® CM3006G-45 | Toray Resin Company | Nylon 66 | Amilan® |
| Hifax CA 1110 G4 LS | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| HiFill® PA6 0365 01 BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Petrothene® NA206000 (Extrusion Coating) | LyondellBasell Industries | LDPE | Petrothene® |
| EnviroPCABS 2010LG | West Michigan Compounding | PC+ABS | EnviroPCABS |