LNP™ VERTON™ PX00700 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1pOkt_LNPVERTONPX00700compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON PX00700 is a compound based on Nylon 6 resin containing Long Glass Fiber. Also known as: LNP* VERTON* Compound PDX-P-00700 Product reorder name: PX00700 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9510 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 188 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.7 | % | ISO 527-2 |
| Flexural Modulus | 8210 | MPa | ISO 178 |
| Flexural Stress | 249 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(23°C) | 32 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 74 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, unannealed, 64.0mm span | 214 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 210 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 299 | °C | |
| Front Temperature | 288 - 299 | °C | |
| Processing (Melt) Temp | 288 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS UG407 - 8229 | AD majoris | Nylon 66 | MAJORIS |
| Axiall PVC 12850 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Flexirene® FG 20 I | Versalis S.p.A. | LLDPE | Flexirene® |
| DURACON® TF-30 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer+PUR | DURACON® |
| POLYfill PP CQX15015 R3 UV | Polykemi AB | PP, Unspecified | POLYfill |