LNP™ STAT-KON™ EX11318C compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y1CXHF_LNP-STAT-KON-EX11318C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON EX11318C is a polyetherimide compound reinforced with carbon fiber for good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding application. A unique feature of this material is its low C18-C40 hydrocarbons. This compound is manufactured using LNP CCS Technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.20 | % | |
| Across Flow : 24 hr | 0.15 to 0.25 | % | |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 21800 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 211 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.9 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 18100 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 380 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 203 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 4.6E-6 | cm/cm/°C | |
| Transverse : -40 to 40°C | 4.3E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 to 5.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+3 to 5.0E+6 | ohms·cm | ASTM D257 |
| Static Decay 6 | 0.1 | sec | FTMS 101B |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 330 to 380 | °C | |
| Middle Temperature | 340 to 380 | °C | |
| Front Temperature | 345 to 380 | °C | |
| Nozzle Temperature | 345 to 380 | °C | |
| Processing (Melt) Temp | 350 to 380 | °C | |
| Mold Temperature | 135 to 165 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PC/ABS PC/ABSFR9002 | Nexus Resin Group, LLC. | PC+ABS | NEXUS PC/ABS |
| AcryliMax 301HP | S&E Specialty Polymers, LLC | ABS | AcryliMax |
| Kingfa PA66-T15 | Kingfa | Nylon 66 | Kingfa |
| KumhoSunny PPO HSP8370 | Shanghai KumhoSunny Plastics Co., Ltd. | PPE+PS | KumhoSunny PPO |
| Pier One POM AH500TF10 NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |