XENOY™ 5720U resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Y15K2O_XENOY5720Uresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.850 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 250°C/2.16 kg | 3.8 | g/10 min | ASTM D1238, ISO 1133 |
| 250°C/5.0 kg | 11 | g/10 min | ASTM D1238, ISO 1133 |
| 265°C/2.16 kg | 6.8 | g/10 min | ASTM D1238 |
| 266°C/5.0 kg | 20 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 3.60 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 10.9 | cm³/10min | ISO 1133 |
| 265°C/2.16 kg | 6.50 | cm³/10min | ISO 1133 |
| 265°C/5.0 kg | 18.9 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.2 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.28 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1830 | MPa | ASTM D638 |
| -- 2 | 1830 | MPa | Internal method |
| -- 3 | 1820 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 44.0 | MPa | ASTM D638 |
| Yield 5 | 45.0 | MPa | Internal method |
| Yield 6 | 47.0 | MPa | ASTM D638 |
| Yield | 44.0 | MPa | ISO 527-2/5 |
| Yield | 47.0 | MPa | ISO 527-2/50 |
| Fracture 7 | 50.0 | MPa | ASTM D638 |
| Fracture 8 | 47.0 | MPa | Internal method |
| Fracture 9 | 48.0 | MPa | ASTM D638 |
| Fracture | 43.0 | MPa | ISO 527-2/5, ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 10 | 4.6 | % | ASTM D638 |
| Yield 11 | 4.6 | % | Internal method |
| Yield 12 | 4.0 | % | ASTM D638 |
| Yield | 4.1 | % | ISO 527-2/5 |
| Yield | 4.6 | % | ISO 527-2/50 |
| Fracture 13 | 120 | % | ASTM D638 |
| Fracture 14 | 110 | % | Internal method |
| Fracture 15 | 120 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2/5 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 16 | 1660 | MPa | ASTM D790 |
| -- 17 | 1870 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 71.0 | MPa | ISO 178 |
| Yield, 50.0mm span 18 | 70.0 | MPa | ASTM D790 |
| Fracture, 50.0mm span 19 | 69.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 20 | ISO 179/1eA | ||
| -30°C | 48 | kJ/m² | ISO 179/1eA |
| 23°C | 56 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -40°C | 600 | J/m | ASTM D256 |
| -30°C | 650 | J/m | ASTM D256 |
| -20°C | 700 | J/m | ASTM D256 |
| -10°C | 660 | J/m | ASTM D256 |
| 0°C | 690 | J/m | ASTM D256 |
| 23°C | 720 | J/m | ASTM D256 |
| -40°C 21 | 46 | kJ/m² | ISO 180/1A |
| -30°C 22 | 48 | kJ/m² | ISO 180/1A |
| -20°C 23 | 50 | kJ/m² | ISO 180/1A |
| -10°C 24 | 52 | kJ/m² | ISO 180/1A |
| 0°C 25 | 55 | kJ/m² | ISO 180/1A |
| 23°C 26 | 56 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Energy at Peak Load | 49.5 | J | ASTM D3763 |
| -40°C, Total Energy | 59.2 | J | ASTM D3763 |
| -30°C, Energy at Peak Load | 49.5 | J | ASTM D3763 |
| -30°C, Total Energy | 61.9 | J | ASTM D3763 |
| -20°C, Energy at Peak Load | 41.9 | J | ASTM D3763 |
| -20°C, Total Energy | 53.2 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 44.8 | J | ASTM D3763 |
| 23°C, Total Energy | 54.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 108 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 6.40mm | 117 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 27 | 110 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 83.5 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 95.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 28 | 87.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 120 | °C | ASTM D1525, ISO 306/B50 15 29 |
| -- | 122 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 95°C | 9.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -30 to 80°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 95°C | 1.0E-4 | cm/cm/°C | ASTM E831 |
| Horizontal : -30 to 80°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 243 - 266 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 254 - 277 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 260 - 277 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 10 mm/min |
| 3 . | 50 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 10mm/min |
| 6 . | Type 1, 50mm/min |
| 7 . | Type 1, 5.0 mm/min |
| 8 . | Type 1, 10mm/min |
| 9 . | Type 1, 50mm/min |
| 10 . | Type 1, 5.0 mm/min |
| 11 . | Type 1, 10mm/min |
| 12 . | Type 1, 50mm/min |
| 13 . | Type 1, 5.0 mm/min |
| 14 . | Type 1, 10mm/min |
| 15 . | Type 1, 50mm/min |
| 16 . | 1.3 mm/min |
| 17 . | 2.0 mm/min |
| 18 . | 1.3 mm/min |
| 19 . | 1.3 mm/min |
| 20 . | 80*10*4 sp=62mm |
| 21 . | 80*10*4 |
| 22 . | 80*10*4 |
| 23 . | 80*10*4 |
| 24 . | 80*10*4 |
| 25 . | 80*10*4 |
| 26 . | 80*10*4 |
| 27 . | 80*10*4 mm |
| 28 . | 80*10*4 mm |
| 29 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Michilene F8100GF20-03 | API Polymers, Inc. | PP Homopolymer | Michilene |
| Bergamid™ A70 G50 H Natural | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ALKAMIX™ MB-PA505 | Marplex Australia Pty. Ltd. | Fluoropolymer | ALKAMIX™ |
| CLEARTUF TURBO II | M&G Gruppo Mossi & Ghisolfi | PET | CLEARTUF |
| Grilon® CF 7 | EMS-GRIVORY | Nylon 6/12 | Grilon® |