Kingfa FRHIPS-8002
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XzSTyQ_Kingfa-FRHIPS-8002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa FRHIPS-8002 is a High Impact Polystyrene material. It is available in Asia Pacific or North America. Important attributes of Kingfa FRHIPS-8002 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, Injection Molded) | 26.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, Injection Molded) | 45 | % | ASTM D638 |
| Flexural Modulus 3(23°C, Injection Molded) | 2250 | MPa | ASTM D790 |
| Flexural Strength 4(23°C, Injection Molded) | 40.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 95 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 78.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.0 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 12 GF 20 H BLACK 96.8001 REC | A. Schulman Europe | Nylon 12 | SCHULAMID® |
| TEKNIFLEX® COC P7P | Tekni-Films, a div of Tekni-Plex | Film, PP/COC/PP | TEKNIFLEX® |
| NatureFlex™ NP 90 | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| LUVOCOM® 16-8960/ES | Lehmann & Voss & Co. | PARA | LUVOCOM® |
| Sumiliteresin® PR-217 | SBHPP | Phenolic | Sumiliteresin® |