POLYFLAM® RIPP 374 ND CS1 5V
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XywIxF_POLYFLAM-RIPP-374-ND-CS1-5V.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% talc filled flame-retardant PP-Copolymer; without PBDE UL94 5VA rated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.39 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 20.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 9.00 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 15 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2500 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| 3.5% strain | 29.0 | MPa | ISO 178 |
| 3.0% strain | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 13 | kJ/m² | ISO 179/1eU |
| 23°C | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 83.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 137 | °C | ISO 306/A50 |
| -- | 59.0 | °C | ISO 306/B50 |
| Ball Pressure Test (100°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 50.0 | °C | UL 746 |
| 3.00 mm | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.750 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 2.00 mm | 5VA | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 960 | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm | 800 | °C | IEC 60695-2-13 |
| 1.50 mm | 800 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 200 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 220 | °C | |
| Processing (Melt) Temp | 180 - 220 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 40.0 - 90.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TARFLON™ SC-253 | Idemitsu Kosan Co., Ltd. | PC+ABS | TARFLON™ |
| TRIEL® HV5401BH | Samyang Corporation | TPEE | TRIEL® |
| EMAC® SP2205 | Westlake Chemical Corporation | EMA | EMAC® |
| Hylex® P1018FRVNHE | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| POTICON NT233B | Otsuka Chemical Co., Ltd. | Nylon 66 | POTICON |