VITAMIDE® BR15OR6337
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XyPGUi_VITAMIDE-BR15OR6337.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BR15OR6337 is a Polyamide 6 (Nylon 6) product filled with 25% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.1 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 135 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 7000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 185 | MPa | ISO 178 |
| Break | 185 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 212 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 218 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 35 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 550 | V | IEC 60112 |
| -- 1 | 550 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 24 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polyvel PLA VB-L01 PLA Antiblock | Polyvel Inc. | PLA | Polyvel PLA |
| Mirathane™ M95 | Miracll Chemicals Co., Ltd. | TPU-Polyether | Mirathane™ |
| TECHNYL® eXten D 218 V30 BLACK | Solvay Engineering Plastics | Nylon 610 | TECHNYL® eXten |
| TAROLOX 10 Z1 G4 | Taro Plast S.p.A. | PBT | TAROLOX |
| Luranyl® KR 2460/3-2 | ROMIRA GmbH | PPE+PS | Luranyl® |