Ultramid® A3ZM2 BK30564
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xy8d4X_Ultramid-A3ZM2-BK30564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid A3ZM2 BK30564 is a specially formulated, non-conductive polyamide based engineering resin for off-line paint applications. The A3ZM2 BK30564 is designed to provide high thermal and chemical resistance, predictable dimensional stability, thin wall processing and a Class A surface. Applications Typical applications include automotive mirror shells and fuel doors and automotive and industrial panels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | 1720 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 51.0 | 38.0 | MPa | |
| Break, 23°C | 49.0 | 37.0 | MPa | |
| Tensile Strain | ISO 527-2 | |||
| Yield, 23°C | 4.1 | 71 | % | |
| Break, 23°C | 15 | 73 | % | |
| Flexural Modulus (23°C) | 2880 | 1730 | MPa | ISO 178 |
| Flexural Stress (23°C) | 86.0 | 50.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 5.4 | 4.5 | kJ/m² | |
| 23°C | 8.5 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 130 | 150 | kJ/m² | |
| 23°C | 160 kJ/m² | No Break | ||
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 5.5 | 4.7 | kJ/m² | |
| 23°C | 8.1 | 11 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 192 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 77.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quantum Composites QC-8100 | Quantum Composites Inc. | Vinyl Ester | Quantum Composites |
| Witcom PA6 2011/342 | Witcom Engineering Plastics B.V. | Nylon 6 | Witcom PA6 |
| Ultra Purge 9010 | Moulds Plus International USA, Inc. | Proprietary | Ultra Purge |
| VALOX™ V4860HR resin | SABIC Innovative Plastics | PBT | VALOX™ |
| ACRYPET® VR S40 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |