GLAMIDE® T-663G50A
| Category: | PARA , Polyarylamide |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XxsToN_GLAMIDE-T-663G50A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE® T-663G50A is a Polyarylamide (PARA) product filled with 50% glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.57 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 to 0.40 | -- | % | |
| 3.00 mm | 0.60 to 0.80 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.30 | -- | % | |
| Equilibrium, 65% RH | 0.80 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 270 | 245 | MPa | |
| Yield, 23°C | 220 | 165 | MPa | |
| Yield, 80°C | 112 | 100 | MPa | |
| Tensile Elongation (Break, 23°C) | 2.0 | 2.2 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 16000 | 15100 | MPa | |
| 23°C | 15000 | 12500 | MPa | |
| 80°C | 7000 | 5900 | MPa | |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 360 | 330 | MPa | |
| Yield, 23°C | 345 | 260 | MPa | |
| Yield, 80°C | 175 | 155 | MPa | |
| Compressive Strength (23°C) | 180 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 140 | 150 | J/m | |
| 23°C | 170 | 190 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 250 | -- | °C | |
| 1.8 MPa, Unannealed | 243 | -- | °C | |
| CLTE - Flow | 1.8E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 25 | 20 | kV/mm | ASTM D149 |
| Arc Resistance | 40.0 | 33.0 | sec | ASTM D495 |
| Comparative Tracking Index | 550 | 550 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 40.0 to 80.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66HSL BK | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Nylene® 600 | Custom Resins Group | Nylon 6 | Nylene® |
| HONES® PPS HS-G40-2 | Guangdong Shunde Hones Polymer Material Co., Ltd. | PPS | HONES® |
| Hostaform® S 9364LPB | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Karina BLACK PVC COMPOUND -E CAK 60-48/ 1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |