KRALASTIC® KU-670 R-2
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | KRALASTIC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XviaQo_KRALASTIC-KU-670-R-2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KRALASTIC® KU-670 R-2 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific or North America for injection molding. Important attributes of KRALASTIC® KU-670 R-2 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 2.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.60 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 116 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 53.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2750 | MPa | ISO 178 |
| Flexural Stress (23°C) | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 102 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 7.5E-5 | cm/cm/°C | JIS K7197 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 230 to 270 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ LH30 | Mando Advanced Materials Co., Ltd. | PP Homopolymer | SEPAZ™ |
| Unipren® Elastomers B3 PRTA010 90A UP317 | Petropol Industry and Trade of Polymers LTDA | PP+EPDM | Unipren® Elastomers |
| Acculam™ Epoxyglas Cowskin™ | Accurate Plastics, Inc. | Epoxy | Acculam™ |
| Fainplast PVC PG 86/AF | Fainplast Compounds S.r.l | PVC+NBR | Fainplast PVC |
| Hifax TYC735X | LyondellBasell Industries | TPO (POE) | Hifax |